self leveling compound flexible

Cementitious Thick Self-leveling

M625
Delivery:
EXW/FOB
minimum order:
1 bag
Supply Ability:
30bag / Day
Country of Origin:
China
Stock Time:
20Day
Quantity:
Contact Now

M625 Cementitious Thick Self-leveling

 

Features:

 
Non-toxic harmless, green and environmental protection;
 
With good construction, fast leveling, high strength.
 
Single construction thickness of 5m-25mm.Low shrinkage, no cracking
 
                Cementitious Thick Self-leveling
Fluidity:≥110mm
Construction temperature:
10-30℃℃
 Mixing ratio:
Powder ( 25kg ) : water ( 5L )
Construction time:
About 6 hours later
Walkable time:
Powder (25 Kg): Water (4.5L-5L)
Flooring may need time :
Waiting for self-leveling completely dry
Compressive strength ( 28 days later ):≥25(MPa)
Flexural strength ( 28 days later ):≥4(MPa)

Product Description:

M625 self leveling cementitious compound, use the special cement, fine aggregate, polymer spray powder resin and other raw materials such as cement additive refined but become.Quick dry self leveling compound have good liquidity, it can fast automatic leveling the ground and is suitable for large and medium-sized civilian residential and public buildings, commercial and industrial buildings, ware.houses,indoor parking lot, such as the fine leveling of the ground at the grass-roots level, The thickness of a single construc.tion can be up to 5m-25mm, at room temperature (above 25'C) and under the condition of good ventilation, it can be used in about 6 hours, The next process can be carried out after self-leveling and completely drying. it can shorten the construction period, provide smooth and sound, solid ideal base. All kinds of elastic floor, ceramic tile, wood floor, carpet, epoxy,polyurethane and other floor materials can be directly pasted on the finished floor.

Substrate Preparation:

The base must be dry, firm, load-bearing, dust-free, no obstruction to bonding sundries, smooth surface;Base without hollow drumwith good compressive strength; In order to ensure good adhesion, the base is sealed with MSYH primer. M318 water-based primer isrecommended for absorbent base and M320 non-absorbent primer is recommended for non-absorbent base.

Construction Method:

①Cleaning up substrate, choose the appropriate primer, when the primer in the dry state (about 2-6 hours after the bottomcoating ),then begin self leveling cementitious compound operation.
②Add 5L water in the mixing container, and then slowly add a pack of 25kg self leveling cementitious compound, stir with a blender to uniform no groug of pulp, pour out the mixture, evenly spread out, with a special toothed scraper to control the thickness, you can use the transportcapacity of 20-40L/min pump slurry, mixture must be used in 20 minutes, prevent direct sunlight and strong wind blowing.
③Before the initial coagulation, the use of special defoaming roll roll to exclude the air, to ensure uniform thickness

Matters Needing Attention:

As quick dry self leveling compound contains cement, it reacts with water to produce strong alkaline, and avoid contact with skin and eyes. Once in contact, flush immediately with water. lf skin or eye is injured, seek medical attention immediately. This product iscompletely hardened and will not produce any material that affects the body or the environment.

Packaging and Storage:

25kg composite paper bag packaging. This product must be stored in the room, pay attention to moisture, prevent freezing exposure, No more than 8 lavers on pallets, Under the condition of aood moisture-proof measures with a shelf life of 6 months.